Skip to main content
banner image
No data available.
Please log in to see this content.
You have no subscription access to this content.
No metrics data to plot.
The attempt to load metrics for this article has failed.
The attempt to plot a graph for these metrics has failed.
The full text of this article is not currently available.
/content/aip/journal/adva/6/5/10.1063/1.4944705
1.
1.T. Nakamura, Y. Nakano, M. Sasagawa, T. Otsuka, M. Aketa, and M. Miura, in 2011 International Symposium on VLSI Design, Automation and Test (2011), pp. 1-2.
http://dx.doi.org/10.1109/VDAT.2011.5783572
2.
2.T. Nomura, H. Kambayashi, M. Masuda, S. Ishii, N. Ikeda, L. Jiang, and S. Yoshida, IEEE Transactions on Electron Devices 53(12), 2908-2913 (2006).
http://dx.doi.org/10.1109/TED.2006.885532
3.
3.W. Stöber and A. Fink, Journal of Colloid and Interface Science 26(1), 6269 (1968).
http://dx.doi.org/10.1016/0021-9797(68)90272-5
5.
5.M. Koeda, A. Harada, H. Ono, T. Ishikura, T. Kuroda, and H. Moro, IEEJ Transactions on Fundamentals and Materials 131(11), 949-954 (2011) (in Japanese).
http://dx.doi.org/10.1541/ieejfms.131.949
6.
6.G. Herzer, IEEE Transactions on Magnetics 26(5), 13971402 (1990).
http://dx.doi.org/10.1109/20.104389
7.
7.A. L. Patterson, Physical Review 56(10), 978-982 (1939).
http://dx.doi.org/10.1103/PhysRev.56.978
http://aip.metastore.ingenta.com/content/aip/journal/adva/6/5/10.1063/1.4944705
Loading
/content/aip/journal/adva/6/5/10.1063/1.4944705
Loading

Data & Media loading...

Loading

Article metrics loading...

/content/aip/journal/adva/6/5/10.1063/1.4944705
2016-03-18
2016-09-26

Abstract

This study focuses on the carbonyl-iron powder (CIP) used in the metal composite bulk magnetic core for high-efficient/light-weight SiC/GaN power device MHz switching dc-dc converter, where the fine CIP with a mean diameter of 1.1 μm is used to suppress the MHz band eddy current inside the CIP body. When applying the CIP to composite core together with the resin matrix, high electrical resistivity layer must be formed on the CIP-surface in order to suppress the overlapped eddy current between adjacent CIPs. In this study, tens nm thick silica (SiO) was successfully deposited on the CIP-surface by using hydrolysis of TEOS (Si(OCH)). Also tens nm thick oxidized layer of the CIP-surface was successfully formed by using CIP annealing in dry air. The SiC/GaN power device can operate at ambient temperature over 200 degree-C, and the composite magnetic core is required to operate at such ambient temperature. The as-made CIP had small coercivity below 800 A/m (10 Oe) due to its nanocrystalline-structure and had a single vortex magnetic structure. From the experimental results, both nanocrystalline and single vortex magnetic structure were maintained after heat-exposure of 250 degree-C, and the powdercoercivity after same heat-exposure was nearly same as that of the as-made CIP. Therefore, the CIP with thermally stable nanocrystalline-structure and vortex magnetic state was considered to be heat-resistant magnetic powder used in the iron-based composite core for SiC/GaN power electronics.

Loading

Full text loading...

/deliver/fulltext/aip/journal/adva/6/5/1.4944705.html;jsessionid=Ci1fyUbOe8sRuzH0M5ijQY39.x-aip-live-06?itemId=/content/aip/journal/adva/6/5/10.1063/1.4944705&mimeType=html&fmt=ahah&containerItemId=content/aip/journal/adva
true
true

Access Key

  • FFree Content
  • OAOpen Access Content
  • SSubscribed Content
  • TFree Trial Content
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
/content/realmedia?fmt=ahah&adPositionList=
&advertTargetUrl=//oascentral.aip.org/RealMedia/ads/&sitePageValue=aipadvances.aip.org/6/5/10.1063/1.4944705&pageURL=http://scitation.aip.org/content/aip/journal/adva/6/5/10.1063/1.4944705'
Right1,Right2,Right3,