Electrical growth of metallic nanoparticles in mesoporous silica films using atomic force microscopy
Rent:
Rent this article for
USD
10.1063/1.4729039
/content/aip/journal/apl/100/24/10.1063/1.4729039
http://aip.metastore.ingenta.com/content/aip/journal/apl/100/24/10.1063/1.4729039
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

Configuration of the experimental set-up used to create silver NP at the mesoporous surface layer.

Image of FIG. 2.
FIG. 2.

Topographic AFM images of the sample surface where silver NP have been grown with a constant contact time (0.3 s). The scale bar is 100 nm. Low and high topography are respectively represented by bright and dark colours. The graph shows the topographic profile of the NP obtained with +9 V. Heights and widths of the NP are resumed in the table.

Image of FIG. 3.
FIG. 3.

Topographic AFM images of the sample surface where silver NP were grown with various contact times. The voltage applied to the AFM tip was constant and equal to +10 V (top images) and −4 V (bottom images). The scale bar is 250 nm (top) and 100 nm (bottom). Low and high topography are respectively represented by bright and dark colours.

Loading

Article metrics loading...

/content/aip/journal/apl/100/24/10.1063/1.4729039
2012-06-13
2014-04-16
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Electrical growth of metallic nanoparticles in mesoporous silica films using atomic force microscopy
http://aip.metastore.ingenta.com/content/aip/journal/apl/100/24/10.1063/1.4729039
10.1063/1.4729039
SEARCH_EXPAND_ITEM