Synthesis and magnetostrictive properties of Pr(Fe1.95B0.05)1.93 bulk nanocrystalline alloy
Rent:
Rent this article for
USD
10.1063/1.4767127
/content/aip/journal/apl/101/19/10.1063/1.4767127
http://aip.metastore.ingenta.com/content/aip/journal/apl/101/19/10.1063/1.4767127

Figures

Image of FIG. 1.
FIG. 1.

The room-temperature XRD patterns of (a)as-spun and (b)-(d) after annealing at under different pressures. (e) The XRD patterns of the annealed as-cast ingots at under 6 GPa.

Image of FIG. 2.
FIG. 2.

The typical AFM micrographs of compounds synthesized under (a) 3 GPa and (b) 6 GPa.

Image of FIG. 3.
FIG. 3.

(a) Magnetization curves and (b) vs H plots for compounds.

Image of FIG. 4.
FIG. 4.

Temperature dependence of magnetization (M-T) for compound synthesized under 6 GPa. The inset shows the plot of dM/dT vs T.

Image of FIG. 5.
FIG. 5.

The room-temperature magnetostriction for compounds synthesized under 3 GPa and 6 GPa.

Tables

Generic image for table
Table I.

The room-temperature magnetostriction (ppm) at different fields for compounds synthesized under 3 GPa and 6 Gpa.

Loading

Article metrics loading...

/content/aip/journal/apl/101/19/10.1063/1.4767127
2012-11-09
2014-04-20
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Synthesis and magnetostrictive properties of Pr(Fe1.95B0.05)1.93 bulk nanocrystalline alloy
http://aip.metastore.ingenta.com/content/aip/journal/apl/101/19/10.1063/1.4767127
10.1063/1.4767127
SEARCH_EXPAND_ITEM