Effects of high-intensity ultrasound on superconductor
Rent:
Rent this article for
USD
10.1063/1.1808500
/content/aip/journal/apl/85/16/10.1063/1.1808500
http://aip.metastore.ingenta.com/content/aip/journal/apl/85/16/10.1063/1.1808500
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

Scanning electron microscope images of (a) initial powder; (b) dried powder after sonication of slurry loading; (c) sintered pellet made from initial powder; (d) sintered pellet made from sonicated material.

Image of FIG. 2.
FIG. 2.

(Color online) Resistance superconducting transition curves normalized by the room temperature value as a function of wt % slurry loading during sonication.

Image of FIG. 3.
FIG. 3.

(Color online) Effect of ultrasonic treatment on BSCCO slurries of various loading, indicated by wt % and arrows. Inset shows critical current density calculated at .

Image of FIG. 4.
FIG. 4.

(Color online) Irreversible magnetization measured at at various temperatures for samples of different slurry loading as described in the text. Right axis—critical current density evaluated by using Bean model.

Image of FIG. 5.
FIG. 5.

(Color online) characteristics measured in reference (left line) and an ultrasonically treated sample (sonicated as a slurry). The enhancement of critical current is estimated about 60%.

Loading

Article metrics loading...

/content/aip/journal/apl/85/16/10.1063/1.1808500
2004-10-22
2014-04-17
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Effects of high-intensity ultrasound on Bi2Sr2CaCu2O8+x superconductor
http://aip.metastore.ingenta.com/content/aip/journal/apl/85/16/10.1063/1.1808500
10.1063/1.1808500
SEARCH_EXPAND_ITEM