High-strength Ti-base ultrafine eutectic with enhanced ductility
Rent:
Rent this article for
USD
10.1063/1.2105998
/content/aip/journal/apl/87/16/10.1063/1.2105998
http://aip.metastore.ingenta.com/content/aip/journal/apl/87/16/10.1063/1.2105998

Figures

Image of FIG. 1.
FIG. 1.

SEM cross-sectional image of as-cast rods for (a) and (b) revealing the change in the morphology of the eutectic up on Sn addition. Inset: XRD patterns corresponding to the microstructures indicating a refinement and decrease in the volume fraction of the phase due to Sn addition.

Image of FIG. 2.
FIG. 2.

TEM bright-field images of as-cast rods: (a) and (b) interrupted growth of the FeTi phase in . Insets: the SAED patterns from the zone axis.

Image of FIG. 3.
FIG. 3.

Room temperature compressive engineering stress-strain curves of the and as-cast rods.

Image of FIG. 4.
FIG. 4.

SEM secondary electron images of the fracture surface: (a) , showing delamination and cutting of the eutectic rods; (b) , revealing that crack path proceeds through the plate shape FeTi phase. Inset: rotation of the eutectic colonies due to interaction with the shear bands (marked by the arrow) at the specimen surface.

Tables

Generic image for table
Table I.

Room temperature compression test results for ( and 3.85): Young’s modulus , yield stress , yield strain , ultimate compression stress , and fracture strain .

Loading

Article metrics loading...

/content/aip/journal/apl/87/16/10.1063/1.2105998
2005-10-12
2014-04-20
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: High-strength Ti-base ultrafine eutectic with enhanced ductility
http://aip.metastore.ingenta.com/content/aip/journal/apl/87/16/10.1063/1.2105998
10.1063/1.2105998
SEARCH_EXPAND_ITEM