Spontaneous formation of ordered nanocrystal arrays in films evaporated onto nanopore array substrates
Rent:
Rent this article for
USD
10.1063/1.2130726
/content/aip/journal/apl/87/19/10.1063/1.2130726
http://aip.metastore.ingenta.com/content/aip/journal/apl/87/19/10.1063/1.2130726
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

(a) SEM images of Pb films on AAO substrates with 34 nm diameter holes with 100 nm center to center spacing . Film thicknesses are indicated in each panel. Inset: Image of a bare substrate. (b) Histogram of the grain size distribution for each film thickness.

Image of FIG. 2.
FIG. 2.

SEM images at two magnifications of the 25-nm-thick Pb film shown in Fig. 1. The grains in the images have the same center to center spacing as the substrate . The inset provides a closeup of the grains that reveals their faceted surfaces .

Image of FIG. 3.
FIG. 3.

SEM images of Pb films on AAO substrates with 80 nm diameter holes and 100 nm center to center hole spacing. Film thicknesses are indicated in each panel. The 0 nm image corresponds to a bare substrate .

Image of FIG. 4.
FIG. 4.

(a) SEM images of a bare substrate and thermally evaporated 20-nm-thick Pd and Au films on AAO substrates with 34 nm diameter holes with 100 nm center to center spacing . (b) Average diameter of the hole openings as a function of film thickness for Au and Pd.

Image of FIG. 5.
FIG. 5.

Close-up view of the SEM image of the 15-nm-thick Pb film shown in Fig. 1. The circles enclose clusters of grains that are presumed to be centered on holes in the substrate .

Loading

Article metrics loading...

/content/aip/journal/apl/87/19/10.1063/1.2130726
2005-11-04
2014-04-23
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Spontaneous formation of ordered nanocrystal arrays in films evaporated onto nanopore array substrates
http://aip.metastore.ingenta.com/content/aip/journal/apl/87/19/10.1063/1.2130726
10.1063/1.2130726
SEARCH_EXPAND_ITEM