Enhancement of the irreversible axial-strain limit of Y-Ba-Cu-O-coated conductors with the addition of a Cu layer
Rent:
Rent this article for
USD
10.1063/1.2136231
/content/aip/journal/apl/87/21/10.1063/1.2136231
http://aip.metastore.ingenta.com/content/aip/journal/apl/87/21/10.1063/1.2136231

Figures

Image of FIG. 1.
FIG. 1.

A comparison of at 76 K and the self-field for YBCO films on Hastalloy C-276 substrates with an IBAD template, with and without a Cu-plated layer. The irreversible strain limit improved substantially for the Cu-plated IBAD-coated conductors.

Image of FIG. 2.
FIG. 2.

A comparison of at 76 K and the self-field for YBCO films on Ni-5at.%W RABiTS, with and without a Cu-laminated layer. The irreversible strain limit improved substantially for the Cu-laminated RABiTS-coated conductors.

Tables

Generic image for table
Table I.

Physical and electromechanical properties of YBCO-coated conductors fabricated by using either Hastalloy-C substrates with an IBAD template or Ni-W RABiTS substrates. Measurements were performed at 76 K. Values of and were determined at a criterion.

Loading

Article metrics loading...

/content/aip/journal/apl/87/21/10.1063/1.2136231
2005-11-18
2014-04-16
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Enhancement of the irreversible axial-strain limit of Y-Ba-Cu-O-coated conductors with the addition of a Cu layer
http://aip.metastore.ingenta.com/content/aip/journal/apl/87/21/10.1063/1.2136231
10.1063/1.2136231
SEARCH_EXPAND_ITEM