Controlled introduction of flux pinning centers in films during pulsed-laser deposition
Rent:
Rent this article for
USD
10.1063/1.2143112
/content/aip/journal/apl/87/26/10.1063/1.2143112
http://aip.metastore.ingenta.com/content/aip/journal/apl/87/26/10.1063/1.2143112
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

Schematic diagram of a PLD target used in the present study showing a small sector made of Y211 in an YBCO target.

Image of FIG. 2.
FIG. 2.

Scanning electron microscope (SEM) micrograph showing the presence of nm sized precipitates (bright white precipitates) present in the YBCO film.

Image of FIG. 3.
FIG. 3.

Scanning electron microscope (SEM) micrographs comparing the microstructures of (a) YBCO and (b) Y211/YBCO films grown in similar conditions on substrates.

Image of FIG. 4.
FIG. 4.

Magnetization measured at 77 K for a control YBCO and the sample with fine precipitates (Y211/YBCO) made using the pie shaped target.

Image of FIG. 5.
FIG. 5.

Magnetization measured at 65 K for three different Y211/YBCO samples compared to a standard YBCO film.

Loading

Article metrics loading...

/content/aip/journal/apl/87/26/10.1063/1.2143112
2005-12-29
2014-04-23
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Controlled introduction of flux pinning centers in YBa2Cu3O7−x films during pulsed-laser deposition
http://aip.metastore.ingenta.com/content/aip/journal/apl/87/26/10.1063/1.2143112
10.1063/1.2143112
SEARCH_EXPAND_ITEM