Effect of oxygen plasma treatment on reduction of contact resistivity at pentacene/Au interface
Rent:
Rent this article for
USD
10.1063/1.2218044
/content/aip/journal/apl/88/26/10.1063/1.2218044
http://aip.metastore.ingenta.com/content/aip/journal/apl/88/26/10.1063/1.2218044

Figures

Image of FIG. 1.
FIG. 1.

Plots of the total resistance between pentacene and Au with various electrode interspacings of TLM patterns. Pentacene film was deposited on bare Au (∎) and on plasma-treated Au (엯).

Image of FIG. 2.
FIG. 2.

Au spectra for (a) bare Au and (b) Au plasma-treated for .

Image of FIG. 3.
FIG. 3.

XRD profiles for thick pentacene films deposited (a) on bare Au and (b) on Au plasma-treated for . The inset shows the theta-rocking curves for pentacene films deposited (c) on bare Au and (d) on Au plasma-treated for . and represent the incident angle of x ray and Bragg reflection angle for (001) plane, respectively.

Image of FIG. 4.
FIG. 4.

Typical C NEXAFS spectra of pentacene films for thicknesses ranging from 1 [(a) and (b)] to [(c) and (d)]. Pentacene films were deposited on bare Au [(a) and (c)] and on Au plasma-treated for [(b) and (d)], respectively.

Tables

Generic image for table
Table I.

Surface energies of Au films with various oxygen plasma treatment times. [ represents the surface energy, and are polar and dispersion components of surface energy, respectively .]

Generic image for table
Table II.

Compositional analysis of Au thin films with oxygen plasma treatment times.

Loading

Article metrics loading...

/content/aip/journal/apl/88/26/10.1063/1.2218044
2006-06-27
2014-04-18
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Effect of oxygen plasma treatment on reduction of contact resistivity at pentacene/Au interface
http://aip.metastore.ingenta.com/content/aip/journal/apl/88/26/10.1063/1.2218044
10.1063/1.2218044
SEARCH_EXPAND_ITEM