Depth-dependent chemical and magnetic local orders in thin magnetic films
Rent this article for
View: Figures


Image of FIG. 1.
FIG. 1.

(Color online) Magnetic hysteresis loops for CoPt films. The main graph shows the loop obtained by extraordinary Hall effect for CoPt10, with the magnetic field perpendicular to the film surface. The insets present the measurements using a vibrating sample magnetometer for CoPt10, CoPt50, and CoPt200, with the external magnetic field planar and perpendicular to the film surface. The data were normalized by the film volume.

Image of FIG. 2.
FIG. 2.

(Color online) (a) XANES experimental data at some typical grazing angles for CoPt50. The lower inset shows the same spectra for CoPt10. (b) XANES ab initio simulations of chemically ordered and disordered CoPt clusters for in-plane polarization.

Image of FIG. 3.
FIG. 3.

(Color online) (a) Asymmetry ratio in XRMS, for a thick film and several incident grazing angles. The different spectra are shifted for clarity. A reference XRMS spectrum obtained for a thick Co film with total planar magnetic anisotropy is shown for comparison in (b).


Article metrics loading...


Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Depth-dependent chemical and magnetic local orders in thin magnetic films