Investigation of electronic structures of ordered and disordered by electron energy loss spectroscopy
Rent:
Rent this article for
USD
10.1063/1.2357028
/content/aip/journal/apl/89/15/10.1063/1.2357028
http://aip.metastore.ingenta.com/content/aip/journal/apl/89/15/10.1063/1.2357028

Figures

Image of FIG. 1.
FIG. 1.

(a) Five overlapped zero-loss EELS spectra acquired from the same area within . The drift of the zero-loss spectra was less than . (b) The sum of four low-loss EELS spectra with energy losses of 0, 10, 20, and .

Image of FIG. 2.
FIG. 2.

TEM images of (a) ordered and (c) disordered . The corresponding SAED patterns are shown in (b) and (d), respectively. (b) shows superlattice reflections and for order structure, while (d) has no superlattice reflections.

Image of FIG. 3.
FIG. 3.

edges of Fe and Ni from ordered (dashed line) and disordered (solid line) , respectively. The threshold energies of the edges of Fe and Ni from disordered phase are lower and higher than those from ordered phase, respectively.

Image of FIG. 4.
FIG. 4.

Normalized Ni edges from ordered (dashed line) and disordered (solid line) as well as Fe edge from pure Fe (dotted line). The inset shows the enlarged Fe edge.

Image of FIG. 5.
FIG. 5.

Normalized Fe edges from ordered (dashed line) and disordered (solid line) . The insets show the enlarged Fe and edges.

Tables

Generic image for table
Table I.

occupancies of disordered , ordered , pure Fe, and pure Ni (unit: ).

Loading

Article metrics loading...

/content/aip/journal/apl/89/15/10.1063/1.2357028
2006-10-12
2014-04-16
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Investigation of electronic structures of ordered and disordered Ni3Fe by electron energy loss spectroscopy
http://aip.metastore.ingenta.com/content/aip/journal/apl/89/15/10.1063/1.2357028
10.1063/1.2357028
SEARCH_EXPAND_ITEM