Solid state reaction at the interface between Heusler alloys and Al cap accelerated by elevated temperature and rough surface
Rent:
Rent this article for
USD
10.1063/1.2805812
/content/aip/journal/apl/91/19/10.1063/1.2805812
http://aip.metastore.ingenta.com/content/aip/journal/apl/91/19/10.1063/1.2805812
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

(Color online) (a) XAS obtained at by total electron yield (, dashed/dotted lines) and transmission (, full lines) for three samples [ is calculated from data with oppositely oriented external field]. Sample I is a -thick film grown on and capped by Al at . Sample II is a -thick Heusler alloy film grown on and capped by Al at . Sample III is a -thick film grown on and capped by Al at . XAS spectra shifted for clarity. (b) Corresponding difference spectra of TEY and TM data. Related dashed/dotted lines as in (a).

Image of FIG. 2.
FIG. 2.

(Color online) (a) XAS obtained at by total electron yield (, dashed/dotted lines) and transmission (, full lines) for three -thick films grown on . Sample IV is a film coated by Al at . Sample V is a film coated by Al at . Sample VI is a film coated by Al at . The spectra are shifted for clarity. (b) Corresponding difference spectra of TEY and TM data for the same sample. Related dashed/dotted lines as in (a).

Image of FIG. 3.
FIG. 3.

(Color online) (a) Gray-level image of of the ratio of the maximum and the intensity of peak of sample VI indicating the content of NiAl. (b) Microspectra acquired in dark spots and surrounding areas of (a).

Loading

Article metrics loading...

/content/aip/journal/apl/91/19/10.1063/1.2805812
2007-11-06
2014-04-18
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Solid state reaction at the interface between Heusler alloys and Al cap accelerated by elevated temperature and rough surface
http://aip.metastore.ingenta.com/content/aip/journal/apl/91/19/10.1063/1.2805812
10.1063/1.2805812
SEARCH_EXPAND_ITEM