Minute pinning and doping additions for strong, , in-field critical current improvement in
Rent:
Rent this article for
USD
10.1063/1.2814060
/content/aip/journal/apl/91/20/10.1063/1.2814060
http://aip.metastore.ingenta.com/content/aip/journal/apl/91/20/10.1063/1.2814060
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

Typical RS sample showing a high density of material.

Image of FIG. 2.
FIG. 2.

(Color online) vs temperature for pure and chemically modified .

Image of FIG. 3.
FIG. 3.

(Color online) vs applied magnetic field for different CS and RS samples. The inset shows nanoparticles in the matrix in a CS sample.

Image of FIG. 4.
FIG. 4.

(Color online) vs applied magnetic field for the optimum RS sample compared to C-doped and -doped from the literature. The inset shows on a linear scale vs field for optimum RS sample compared to a C-doped sample.

Loading

Article metrics loading...

/content/aip/journal/apl/91/20/10.1063/1.2814060
2007-11-15
2014-04-20
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Minute pinning and doping additions for strong, 20K, in-field critical current improvement in MgB2
http://aip.metastore.ingenta.com/content/aip/journal/apl/91/20/10.1063/1.2814060
10.1063/1.2814060
SEARCH_EXPAND_ITEM