Tuning the perpendicular magnetic anisotropy in tetragonally distorted alloy films on Rh (001) by varying the alloy composition
Rent:
Rent this article for
USD
10.1063/1.2821370
/content/aip/journal/apl/91/26/10.1063/1.2821370
http://aip.metastore.ingenta.com/content/aip/journal/apl/91/26/10.1063/1.2821370
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

STM images of (a) Rh (001) with scale ; and alloy films on Rh with (b) 0.8 ML, (c) 2.9 ML, and (d) 4.2 ML. The scale is .

Image of FIG. 2.
FIG. 2.

LEED curve of the (0, 0) spot as a function of incident electron energy on Rh (001) as well as alloy films with different thicknesses. The lower panel shows the Kikuchi patterns of (a) Rh (001) and (b) 7 ML , combined with LEED patterns of (c) Rh (001) and (d) 7 ML .

Image of FIG. 3.
FIG. 3.

Series of polar MOKE loops of alloy films on Rh (001) with different thicknesses measured at room temperature.

Image of FIG. 4.
FIG. 4.

(a) Regions of perpendicular and in-plane easy axis of magnetization measured at room temperature for alloys at room temperature grown on Pd (001) and Rh (001), respectively. (b) The of alloy film grown on Pd (001) as a function of film thickness.

Loading

Article metrics loading...

/content/aip/journal/apl/91/26/10.1063/1.2821370
2007-12-27
2014-04-24
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Tuning the perpendicular magnetic anisotropy in tetragonally distorted FexCo1−x alloy films on Rh (001) by varying the alloy composition
http://aip.metastore.ingenta.com/content/aip/journal/apl/91/26/10.1063/1.2821370
10.1063/1.2821370
SEARCH_EXPAND_ITEM