Heteroepitaxial growth of ferromagnetic rutile on GaN (0001)
Rent:
Rent this article for
USD
10.1063/1.2838297
/content/aip/journal/apl/92/4/10.1063/1.2838297
http://aip.metastore.ingenta.com/content/aip/journal/apl/92/4/10.1063/1.2838297

Figures

Image of FIG. 1.
FIG. 1.

XRD pattern of the film grown on GaN (0001) at (sample B). The inset is a rocking curve of rutile (200) peak of the sample.

Image of FIG. 2.
FIG. 2.

curves of at room temperature. The magnetic field was applied perpendicular to the film surface.

Image of FIG. 3.
FIG. 3.

(a) Cross-sectional TEM image of the film grown on GaN (0001) at (sample B). (b) High-resolution image of the interface.

Image of FIG. 4.
FIG. 4.

Comparison of the curve (solid line) and the curve (dashed line) of samples A and B at room temperature. The curve was measured by a conventional SQUID magnetometer (Quantum Design MPMS XL5) and the magnetic field was applied perpendicular to the film surface.

Tables

Generic image for table
Table I.

and values of films fabricated on semi-insulating GaN (0001) at different . The transport data were evaluated by the standard six-probe method.

Loading

Article metrics loading...

/content/aip/journal/apl/92/4/10.1063/1.2838297
2008-01-28
2014-04-24
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Heteroepitaxial growth of ferromagnetic rutile CoxTi1−xO2−δ on GaN (0001)
http://aip.metastore.ingenta.com/content/aip/journal/apl/92/4/10.1063/1.2838297
10.1063/1.2838297
SEARCH_EXPAND_ITEM