Direct observation of individual Barkhausen avalanches in nucleation-mediated magnetization reversal processes
Rent:
Rent this article for
USD
10.1063/1.3256188
/content/aip/journal/apl/95/18/10.1063/1.3256188
http://aip.metastore.ingenta.com/content/aip/journal/apl/95/18/10.1063/1.3256188
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

Typical magnetic domain configurations of the alloy film recorded at the Co x-ray absorption edge (777 eV) with applied magnetic fields of (a), (b), (c), (d)0, and (e)−200 Oe. (f) M vs H hysteresis loop obtained via VSM measurement.

Image of FIG. 2.
FIG. 2.

(a) Distributions of Barkhausen avalanches observed in the field steps I, II, III, and IV. (b) Two repetitive cyclic measurements in the exactly identical area of the sample.

Image of FIG. 3.
FIG. 3.

Distributions of the Barkhausen avalanche size taken in the field steps (a) I, (b) II, (c) III, and (d) IV along the hysteresis loop in alloy film, where each distribution was determined from the statistical analysis of more than 700 Barkhausen avalanche sizes. The inserted images are superimposed domain configurations taken at the initial and final fields of each step.

Loading

Article metrics loading...

/content/aip/journal/apl/95/18/10.1063/1.3256188
2009-11-03
2014-04-21
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Direct observation of individual Barkhausen avalanches in nucleation-mediated magnetization reversal processes
http://aip.metastore.ingenta.com/content/aip/journal/apl/95/18/10.1063/1.3256188
10.1063/1.3256188
SEARCH_EXPAND_ITEM