Texture inheritance in thin-film growth of
Rent:
Rent this article for
USD
10.1063/1.3192357
/content/aip/journal/apl/95/4/10.1063/1.3192357
http://aip.metastore.ingenta.com/content/aip/journal/apl/95/4/10.1063/1.3192357
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

SEM micrographs on cross sections of the ZnS precursors after different times of evaporation at 650 K. The bars mark .

Image of FIG. 2.
FIG. 2.

STEM-EDX depth profile on a cross section of the ZnS precursor after 5.5 min of evaporation.

Image of FIG. 3.
FIG. 3.

Pole figures for different diffracting planes of the ZnS precursor after 2.5 min of evaporation. The intensity rings are typical for a fiber texture in a cubic system (theoretical interplanar angle of {111} planes: 70.5°, theoretical interplanar angle of {111} and {200} planes: 54.7°).

Image of FIG. 4.
FIG. 4.

Pole figures for different diffracting planes of the layer after 20.5 min of evaporation. The intensity rings indicate a double fiber texture in the directions and .

Image of FIG. 5.
FIG. 5.

HRTEM micrograph of the interface after 5.5 min of processing. The arrows mark the normals of the observed lattice planes. The dotted lines mark the grain boundaries. The planes of the grain are tilted more than 15° with respect to the ZnS planes.

Loading

Article metrics loading...

/content/aip/journal/apl/95/4/10.1063/1.3192357
2009-07-29
2014-04-24
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Texture inheritance in thin-film growth of Cu2ZnSnS4
http://aip.metastore.ingenta.com/content/aip/journal/apl/95/4/10.1063/1.3192357
10.1063/1.3192357
SEARCH_EXPAND_ITEM