Formation of long-range ordered quantum dots arrays in amorphous matrix by ion beam irradiation
Rent:
Rent this article for
USD
10.1063/1.3204007
/content/aip/journal/apl/95/6/10.1063/1.3204007
http://aip.metastore.ingenta.com/content/aip/journal/apl/95/6/10.1063/1.3204007
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

(a) TEM cross sections of the ML after ion-beam irradiation of the as-deposited ML. Arrows indicate irradiation direction. [(b) and (c)] TEM images of the same ML after annealing (two different magnifications). The inset in panel (c) shows the Fourier transformation of the measured TEM image.

Image of FIG. 2.
FIG. 2.

Geometry of GISAXS measurements. Irradiation directions are indicated by red arrows. The incident x-ray beam is (a) parallel and (b) perpendicular to the irradiation plane. are the reciprocal-space coordinates.

Image of FIG. 3.
FIG. 3.

GISAXS maps measured on (a) as-deposited (AS) ML, [(b) and (c)] irradiated (IRR) ML in and configurations, respectively. (d) Simulation (sim) of the map shown in (c). Measured (e) and simulated (f) map of the irradiated ML after annealing at . The linear intensity scale is indicated in panel (e). The narrow horizontal sheet in (e) at is a dynamical umweganregung effect (Ref. 9) that has not been included in the simulation.

Loading

Article metrics loading...

/content/aip/journal/apl/95/6/10.1063/1.3204007
2009-08-11
2014-04-20
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Formation of long-range ordered quantum dots arrays in amorphous matrix by ion beam irradiation
http://aip.metastore.ingenta.com/content/aip/journal/apl/95/6/10.1063/1.3204007
10.1063/1.3204007
SEARCH_EXPAND_ITEM