Experimental evidence for orientation property of by manipulating polar axis angle using substrate
Rent:
Rent this article for
USD
10.1063/1.3357421
/content/aip/journal/apl/96/10/10.1063/1.3357421
http://aip.metastore.ingenta.com/content/aip/journal/apl/96/10/10.1063/1.3357421

Figures

Image of FIG. 1.
FIG. 1.

XRD results [(a), (b), and (c)] and XRD reciprocal space mapping near PZT (d) 002, (e) 202, and (f) 222 for PZT films grown on substrates covered with [(a) and (d)], [(b) and (e)], and [(c) and (f)]-oriented layers.

Image of FIG. 2.
FIG. 2.

Room temperature hysteresis loops of PZT films measured at 1 kHz. (a) (001), (b) (101), and (c) (111) PZT films grown on substrates. (d) (100)/(001), (e) (101)/(110), and (f) (111)-oriented PZT films grown on substrates.

Image of FIG. 3.
FIG. 3.

(a) Tilt angle dependency of PZT films grown on substrates. The tilt angle of the plane of the pseudocubic layers from the in-plane direction was defined as . Hence the orientation corresponds to , to , and to . (Closed circles): measured values. (Open squares): Estimated values, calculated from the polarization vector and the (b) tilt angle dependency in PZT films grown on substrates. (Closed circles): Measured values. (Open squares): values estimated from the polarization vector and the volume fractions, , , and in Table I. Continuous lines in (a) and (b) show the data for polar-axis oriented films (Ref. 7).

Tables

Generic image for table
Table I.

Volume fraction of PZT films grown with various orientations and kinds of substrates.

Loading

Article metrics loading...

/content/aip/journal/apl/96/10/10.1063/1.3357421
2010-03-09
2014-04-24
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Experimental evidence for orientation property of Pb(Zr0.35Ti0.65)O3 by manipulating polar axis angle using CaF2 substrate
http://aip.metastore.ingenta.com/content/aip/journal/apl/96/10/10.1063/1.3357421
10.1063/1.3357421
SEARCH_EXPAND_ITEM