Large exchange bias field in the Ni–Mn–Sn Heusler alloys with high content of Mn
Rent:
Rent this article for
USD
10.1063/1.3428782
/content/aip/journal/apl/96/20/10.1063/1.3428782
http://aip.metastore.ingenta.com/content/aip/journal/apl/96/20/10.1063/1.3428782

Figures

Image of FIG. 1.
FIG. 1.

ZFC and FC magnetization curves as a function of temperature for alloy under a magnetic field of 100 Oe.

Image of FIG. 2.
FIG. 2.

Magnetic hysteresis loops of alloy measured at different temperatures.

Image of FIG. 3.
FIG. 3.

Magnetic hysteresis loops of (, 0.5, and 1) alloys measured at 2 K. Inset shows the enlarged view of the EB field.

Image of FIG. 4.
FIG. 4.

EB field and coercive field of (, 0.5, and 1) alloys as a function of temperature.

Tables

Generic image for table
Table I.

The crystallographic sites that Mn atoms would occupy and the type of exchange coupling between the moments of Mn on different sites and those on the regular Mn sites.

Loading

Article metrics loading...

/content/aip/journal/apl/96/20/10.1063/1.3428782
2010-05-17
2014-04-24
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Large exchange bias field in the Ni–Mn–Sn Heusler alloys with high content of Mn
http://aip.metastore.ingenta.com/content/aip/journal/apl/96/20/10.1063/1.3428782
10.1063/1.3428782
SEARCH_EXPAND_ITEM