Enhancement of plastic deformability in Fe–Ni–Nb–B bulk glassy alloys by controlling the Ni-to-Fe concentration ratio
Rent:
Rent this article for
USD
10.1063/1.3291668
/content/aip/journal/apl/96/3/10.1063/1.3291668
http://aip.metastore.ingenta.com/content/aip/journal/apl/96/3/10.1063/1.3291668

Figures

Image of FIG. 1.
FIG. 1.

XRD and DSC traces obtained from as-cast alloys with , 0.25, and 0.5, respectively.

Image of FIG. 2.
FIG. 2.

Room temperature compressive engineering stress-strain curves obtained from the ( and 0.5) samples.

Image of FIG. 3.
FIG. 3.

Secondary electron SEM images taken from the deformed (before failure) and failed samples ( and 0.5): (a) outer surface, [(b) and (c)] fracture surface morphologies of sample; [(d) and (e)] lateral surface morphologies of deformed sample; and (f) fracture surface morphology of failed sample for the sample, respectively. The insets in (e) and (f) show a highly magnified image for the dashed circle region in (e) and the outer shape of the failed sample, respectively.

Image of FIG. 4.
FIG. 4.

High-resolution TEM images and corresponding FFT patterns of the as-cast rod samples with and 0.5, respectively.

Tables

Generic image for table
Table I.

Compressive mechanical properties, density, and elastic constants for the as-cast alloys with , 0.25, and 0.5, yield stress , yield strain , ultimate compressive stress , plastic strain , density , Poisson’s ratio , Young’s modulus , shear modulus , and bulk modulus .

Loading

Article metrics loading...

/content/aip/journal/apl/96/3/10.1063/1.3291668
2010-01-19
2014-04-16
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Enhancement of plastic deformability in Fe–Ni–Nb–B bulk glassy alloys by controlling the Ni-to-Fe concentration ratio
http://aip.metastore.ingenta.com/content/aip/journal/apl/96/3/10.1063/1.3291668
10.1063/1.3291668
SEARCH_EXPAND_ITEM