Magnetization reversal process in Fe/FePt films
Rent:
Rent this article for
USD
10.1063/1.3293444
/content/aip/journal/apl/96/3/10.1063/1.3293444
http://aip.metastore.ingenta.com/content/aip/journal/apl/96/3/10.1063/1.3293444
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

In-plane and out-of-plane magnetic hysteresis loops of (a) FePt single layer annealed at for 10 min. The Fe/FePt bilayer with different Fe layer thickness, (b) 3 nm, (c) 6 nm, and (d) 15 nm (FePt layer was annealed at for 10 min, Fe layer was deposited at room temperature).

Image of FIG. 2.
FIG. 2.

The theoretical (see Ref. 22) and experimental optimal exchange-coupling and resulting switching field as function of the ratio.

Image of FIG. 3.
FIG. 3.

TEM images, grains size distribution, and SAD patterns of (a) FePt single layer annealed at for 10 min. (This film was not covered by ) (b) Fe/FePt bilayer with Fe thickness 3 nm (c) Fe/FePt bilayer with Fe thickness 6 nm.

Loading

Article metrics loading...

/content/aip/journal/apl/96/3/10.1063/1.3293444
2010-01-22
2014-04-21
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Magnetization reversal process in Fe/FePt films
http://aip.metastore.ingenta.com/content/aip/journal/apl/96/3/10.1063/1.3293444
10.1063/1.3293444
SEARCH_EXPAND_ITEM