Spin and orbital magnetic moments of molecular beam epitaxy films on and MgO(001) substrates by x-ray magnetic circular dichroism
Rent:
Rent this article for
USD
10.1063/1.3564887
/content/aip/journal/apl/98/10/10.1063/1.3564887
http://aip.metastore.ingenta.com/content/aip/journal/apl/98/10/10.1063/1.3564887

Figures

Image of FIG. 1.
FIG. 1.

curves of samples A and B measured by a SQUID magnetometer at 300 K. The external magnetic field applied was parallel to the sample surface.

Image of FIG. 2.
FIG. 2.

XAS and XMCD spectra of samples A and B observed at 300 K. The external magnetic field was perpendicular to the sample surface.

Image of FIG. 3.
FIG. 3.

dependence of element-specific XMCD intensities for Fe and N atoms in sample C measured at 100 K. The external magnetic field was applied perpendicular to the sample surface.

Tables

Generic image for table
Table I.

Spin and orbital magnetic moments of iron nitrides and deduced by experimental and theoretical analyses.

Loading

Article metrics loading...

/content/aip/journal/apl/98/10/10.1063/1.3564887
2011-03-10
2014-04-21
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Spin and orbital magnetic moments of molecular beam epitaxy γ′-Fe4N films on LaAlO3(001) and MgO(001) substrates by x-ray magnetic circular dichroism
http://aip.metastore.ingenta.com/content/aip/journal/apl/98/10/10.1063/1.3564887
10.1063/1.3564887
SEARCH_EXPAND_ITEM