: A possible high-temperature soft magnetic material and strongly correlated system
Rent this article for
View: Figures


Image of FIG. 1.
FIG. 1.

(a) XRD pattern for around room temperature. Left inset: enlargement of XRD pattern around the (220) peak for . Right inset: lattice parameters of at various temperatures obtained from the Rietveld refinements. (b) Temperature dependent magnetization curve under FC process at 100 Oe from 5 to 850 K. Top inset: the refined lattice parameter and the Curie temperature for . Bottom inset: isotherm magnetization curves at 5 K for .

Image of FIG. 2.
FIG. 2.

(a) Temperature dependent resistivity of at zero field from 5 K to 850 K. Left inset: temperature dependence of resistivity from 5 K to 350 K at 0 Oe and 50 kOe, respectively; right inset: nonlinear fitting of below 30 K. (b) Specific heat for at zero field. Inset: is plotted as a function of . The solid line indicates the fitting to Eq. (1).

Image of FIG. 3.
FIG. 3.

(a) Temperature dependence of Seebeck coefficient at zero field. (b) Thermal conductivity as a function of temperature at zero field.


Article metrics loading...


Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: AlNxMn3: A possible high-temperature soft magnetic material and strongly correlated system