Positive exchange bias from magnetization reversal in La1−xPrxCrO3 (x ∼ 0.7–0.85)
Rent:
Rent this article for
USD
10.1063/1.3644473
/content/aip/journal/apl/99/14/10.1063/1.3644473
http://aip.metastore.ingenta.com/content/aip/journal/apl/99/14/10.1063/1.3644473
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

(Color online) (a) Magnetization (M) plotted against temperature (T) for La0.15Pr0.85CrO3, measured in field-cooled mode with applied field (H) of 20 Oe. Squares show experimental data, and solid line shows the fitting. Inset shows region near compensation temperature T comp. (b) Magnetic susceptibility (χ = M/H) plotted against T for several H values for La0.15Pr0.85CrO3. (c) Magnetization-magnetic field (MH) curves at 10 K with cooling fields (H cool) of 10 kOe and 2 kOe for La0.15Pr0.85CrO3. Arrows indicate shifts in coercivity. (b) MH curve at 200 K with H cool = 2 kOe for La0.15Pr0.85CrO3. Arrow indicates shift in coercivity.

Image of FIG. 2.
FIG. 2.

(Color online) EB field (H EB) plotted against temperature (T) for several H cool values for La0.15Pr0.85CrO3. Inset shows training effect at 100 K for H cool = 2 kOe. Squares show experimental data, and solid line shows the fitting.

Image of FIG. 3.
FIG. 3.

(Color online) (a) Direction of Pr3+ moments with respect to Cr3+ canted component (M Cr; Eq. (1)). (A) and (B) are associated with PEB or NEB, respectively. (b) H EB plotted against temperature (T) for several H cool values for La0.25Pr0.75CrO3 (H I ∼ 15–16 kOe; Eq. (1)).

Loading

Article metrics loading...

/content/aip/journal/apl/99/14/10.1063/1.3644473
2011-10-04
2014-04-20
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Positive exchange bias from magnetization reversal in La1−xPrxCrO3 (x ∼ 0.7–0.85)
http://aip.metastore.ingenta.com/content/aip/journal/apl/99/14/10.1063/1.3644473
10.1063/1.3644473
SEARCH_EXPAND_ITEM