X-ray magnetic circular dichroism of ferromagnetic Co4N epitaxial films on SrTiO3(001) substrates grown by molecular beam epitaxy
Rent:
Rent this article for
USD
10.1063/1.3670353
/content/aip/journal/apl/99/25/10.1063/1.3670353
http://aip.metastore.ingenta.com/content/aip/journal/apl/99/25/10.1063/1.3670353

Figures

Image of FIG. 1.
FIG. 1.

(Color online) (a) XAS and (b) XMCD spectra at the Co L 2,3 edges of samples A and B observed at 300 K. The external magnetic field (H = ±4 T) was applied perpendicular to the sample surface.

Image of FIG. 2.
FIG. 2.

(Color online) (a) XAS and (b) XMCD spectra at the N K absorption edge of sample A observed at 300 K. The external magnetic field (H = ±4 T) was applied perpendicular to the sample surface.

Image of FIG. 3.
FIG. 3.

(Color online) H dependence of element-specific XMCD intensities for Co and N atoms in sample A measured at 300 K. The external magnetic field was applied perpendicular to the sample surface.

Tables

Generic image for table
Table I.

Orbital, spin, and total magnetic moments of Co4N and hcp-Co deduced by experimental and theoretical analyses. Corrected moment values of samples after taking the saturation effect into account are listed in parentheses.

Loading

Article metrics loading...

/content/aip/journal/apl/99/25/10.1063/1.3670353
2011-12-19
2014-04-19
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: X-ray magnetic circular dichroism of ferromagnetic Co4N epitaxial films on SrTiO3(001) substrates grown by molecular beam epitaxy
http://aip.metastore.ingenta.com/content/aip/journal/apl/99/25/10.1063/1.3670353
10.1063/1.3670353
SEARCH_EXPAND_ITEM