Temperature dependence of magnetoresistivity of cobalt-polytetrafluoroethylene granular composite films
Rent:
Rent this article for
USD
10.1063/1.2821240
/content/aip/journal/jap/102/11/10.1063/1.2821240
http://aip.metastore.ingenta.com/content/aip/journal/jap/102/11/10.1063/1.2821240
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

SEM micrographs of the cobalt-PTFE film produced by PLD (a) before etching and (b) after etching with HCl .

Image of FIG. 2.
FIG. 2.

Temperature dependence of the resistance of cobalt-PTFE composite film. The inset is a plot of against .

Image of FIG. 3.
FIG. 3.

Magnetic field dependence of the magnetoresistance of the cobalt-PTFE composite film with (a) out-of-plane measurement and (b) in-plane measurement.

Image of FIG. 4.
FIG. 4.

Magnetic field dependence of the magnetoresistance of the cobalt-PTFE composite film measured at (a) 20 and (b) , both are with in-plane measurements.

Image of FIG. 5.
FIG. 5.

Temperature dependence of the separations of the MR peaks at a temperature range from .

Image of FIG. 6.
FIG. 6.

(Color online) Temperature dependence of MR of two cobalt-PTFE composite films fabricated by a cobalt:PTFE laser pulse ratio of 30:2 and 34:2 respectively, measured at the applied magnetic field of .

Loading

Article metrics loading...

/content/aip/journal/jap/102/11/10.1063/1.2821240
2007-12-04
2014-04-23
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Temperature dependence of magnetoresistivity of cobalt-polytetrafluoroethylene granular composite films
http://aip.metastore.ingenta.com/content/aip/journal/jap/102/11/10.1063/1.2821240
10.1063/1.2821240
SEARCH_EXPAND_ITEM