Ferromagnetic fraction and exchange anisotropy in SUS 316LN austenitic stainless steel due to strain-induced deformation
Rent:
Rent this article for
USD
10.1063/1.2830831
/content/aip/journal/jap/103/7/10.1063/1.2830831
http://aip.metastore.ingenta.com/content/aip/journal/jap/103/7/10.1063/1.2830831

Figures

Image of FIG. 1.
FIG. 1.

Magnetization of the undeformed sample indicating the paramagnetic and antiferromagnetic behaviors as a function of temperature.

Image of FIG. 2.
FIG. 2.

Volume fraction of strain-induced martensite (FM) due to compressive deformation at RT. The inset shows the saturation magnetization plots measured at RT and after subtracting the magnetization of the austenitic matrix.

Image of FIG. 3.
FIG. 3.

as a function of FM volume fraction at . The top inset is the enlarged view of the loops, and the bottom inset is the vs for the sample deformed to .

Tables

Generic image for table
Table I.

Chemical composition of SUS 316LN (wt %).

Loading

Article metrics loading...

/content/aip/journal/jap/103/7/10.1063/1.2830831
2008-01-24
2014-04-25
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Ferromagnetic fraction and exchange anisotropy in SUS 316LN austenitic stainless steel due to strain-induced deformation
http://aip.metastore.ingenta.com/content/aip/journal/jap/103/7/10.1063/1.2830831
10.1063/1.2830831
SEARCH_EXPAND_ITEM