Ferromagnetism in tetragonally distorted thin films
Rent:
Rent this article for
USD
10.1063/1.3059606
/content/aip/journal/jap/105/7/10.1063/1.3059606
http://aip.metastore.ingenta.com/content/aip/journal/jap/105/7/10.1063/1.3059606
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

Reciprocal space maps at the (103) peak of LCO films on STO showing both in-plane and out-of-plane axes.

Image of FIG. 2.
FIG. 2.

Dependence of the out-of-plane lattice parameter, , on the oxygen pressure during deposition for films grown on STO (orange triangles) and LSAT substrates (blue circles). The inset shows scans of films grown in high (black) and low (orange) oxygen pressures on STO.

Image of FIG. 3.
FIG. 3.

(Top) XA spectra measured at for (orange, open circles) and (black, closed triangles) LCO films grown on Nb:STO. (Bottom) XMCD difference signal showing increased dichroism from sample at the peak.

Image of FIG. 4.
FIG. 4.

Temperature dependence of the magnetization for LCO films grown in (orange) and (black) of oxygen on STO. The films were field cooled and then measured in an applied field of . Inset shows magnetization vs applied field measurements taken at .

Loading

Article metrics loading...

/content/aip/journal/jap/105/7/10.1063/1.3059606
2009-02-06
2014-04-25
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Ferromagnetism in tetragonally distorted LaCoO3 thin films
http://aip.metastore.ingenta.com/content/aip/journal/jap/105/7/10.1063/1.3059606
10.1063/1.3059606
SEARCH_EXPAND_ITEM