The intermixing induced perpendicular magnetic anisotropy in ultrathin Co/Pt multilayers
Rent:
Rent this article for
USD
10.1063/1.3070639
/content/aip/journal/jap/105/7/10.1063/1.3070639
http://aip.metastore.ingenta.com/content/aip/journal/jap/105/7/10.1063/1.3070639
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

X-ray diffraction patterns of multilayer systems with Co thickness ranging from 0.83 to 2.08 nm for incident grazing angle .

Image of FIG. 2.
FIG. 2.

(a) Cross-sectional and (b) plane-view HRTEM micrographs of sample with 2.08 nm Co thickness

Image of FIG. 3.
FIG. 3.

(a) Cross-sectional and (b) plane-view HRTEM micrographs of sample with 0.83 nm Co thickness. The inset in (a) represents the example of image simulation, which was used to identify the phase in the analysis of HRTEM.

Image of FIG. 4.
FIG. 4.

Domain images of the samples shown in (a) Fig. 2 and (b) Fig. 3.

Image of FIG. 5.
FIG. 5.

loops of samples shown in Figs. 2 and 3.

Image of FIG. 6.
FIG. 6.

Dependence of the effective anisotropy and magnetoelastic anisotropy on the Co thickness, . The insets are schematic plots, which identify that onset of intermixing and PMA when is around 1 nm.

Loading

Article metrics loading...

/content/aip/journal/jap/105/7/10.1063/1.3070639
2009-04-06
2014-04-17
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: The intermixing induced perpendicular magnetic anisotropy in ultrathin Co/Pt multilayers
http://aip.metastore.ingenta.com/content/aip/journal/jap/105/7/10.1063/1.3070639
10.1063/1.3070639
SEARCH_EXPAND_ITEM