Effect of film texture on magnetization reversal and switching field in continuous and patterned (Co/Pd) multilayers
Rent:
Rent this article for
USD
10.1063/1.3173546
/content/aip/journal/jap/106/2/10.1063/1.3173546
http://aip.metastore.ingenta.com/content/aip/journal/jap/106/2/10.1063/1.3173546
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

Hysteresis loops measured from polar MOKE for three samples deposited at different Ar pressures.

Image of FIG. 2.
FIG. 2.

The coercivity and the full width half maximum, , of (Co/Pd) multilayers as a function of the deposition argon pressure.

Image of FIG. 3.
FIG. 3.

Normalized magnetization vs normalized applied field to the coercivity for nonpatterned samples deposited at different argon pressures. The larger the deposition pressure the narrow the switching field is.

Image of FIG. 4.
FIG. 4.

MFM images of taken at remanence states after removing the applied field indicated on each figure. The top series of images are for the sample deposited at 1.5 mTorr with of 5.1°. The bottom series of images are for the sample deposited at 5 mTorr deposition pressure and having of 3.8°.

Image of FIG. 5.
FIG. 5.

Switching probability as a function of applied field for samples deposited at 1.5, 3, and 5 mTorr. No major difference in switching probability for samples deposited at 3 and 5 mTorr but 50% of the number of dots switched at larger field compared to the sample deposited at low pressure of 1.5 mTorr.

Image of FIG. 6.
FIG. 6.

SFD for the three samples shown in Fig. 6. The applied field is normalized to their respective coercivities.

Loading

Article metrics loading...

/content/aip/journal/jap/106/2/10.1063/1.3173546
2009-07-17
2014-04-20
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Effect of film texture on magnetization reversal and switching field in continuous and patterned (Co/Pd) multilayers
http://aip.metastore.ingenta.com/content/aip/journal/jap/106/2/10.1063/1.3173546
10.1063/1.3173546
SEARCH_EXPAND_ITEM