Effect of strong gravity on superconductor
Rent:
Rent this article for
USD
10.1063/1.3475519
/content/aip/journal/jap/108/5/10.1063/1.3475519
http://aip.metastore.ingenta.com/content/aip/journal/jap/108/5/10.1063/1.3475519

Figures

Image of FIG. 1.
FIG. 1.

Thin-plate type sample setup in a rotor.

Image of FIG. 2.
FIG. 2.

Electron probe micro analysis color mappings and SEM image of the initial sample (a) and electron probe micro analysis color mappings and SEM image at a polished surface containing the rotation axis of the ultracentrifuge-treated twinned single crystal (temperature: , time: 24 h).

Image of FIG. 3.
FIG. 3.

Polarized microscope images of the initial sample (a), ultracentrifuged sample (temperature: , time: 24 h) (b), and green transparent single crystal (c).

Image of FIG. 4.
FIG. 4.

XRD patterns (G1 and G2) of a microarea (0.1 mm) from the right edge of the sample along the straight line (Fig. 3) area with indicated ◼ Y123 and ●Y211 Phases (lower gravity area).

Image of FIG. 5.
FIG. 5.

The powder XRD patterns of higher gravity area with (a) and (b) indicated ◼ Y123, ● Y211, and ▲ phases (higher gravity area).

Image of FIG. 6.
FIG. 6.

Lattice parameters (nm) in (a), (nm) in (b). and (nm) in (c) of Y123 phase obtained by the XRD patterns of the sample through the gravity direction including with initial sample and unit cell volumes (cubic nanometer) of Y123 phase using lattice parameters compared with initial and experimental sample in (d).

Image of FIG. 7.
FIG. 7.

The graphs of the volume magnetization vs temperature of the initial and experimental samples (lower gravity layer and higher gravity layer) (a); and experimental sample (b).

Tables

Generic image for table
Table I.

Experimental conditions.

Generic image for table
Table II.

Experimental details of crystal refinement of Y211.

Generic image for table
Table III.

Atomic coordinates (in units of ) and equivalent thermal parameter.

Generic image for table
Table IV.

The average metal to oxygen distances (nm), lattice constants (nm), and unit cell volume in Y211 at room temperature.

Generic image for table
Table V.

Metal to oxygen distances (Å) in Y211 at room temperature.

Loading

Article metrics loading...

/content/aip/journal/jap/108/5/10.1063/1.3475519
2010-09-13
2014-04-24
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Effect of strong gravity on Y1Ba2Cu3O7−x superconductor
http://aip.metastore.ingenta.com/content/aip/journal/jap/108/5/10.1063/1.3475519
10.1063/1.3475519
SEARCH_EXPAND_ITEM