Electrical annealing for flexible organic light-emitting diodes having poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) anodes
Rent:
Rent this article for
USD
10.1063/1.3499286
/content/aip/journal/jap/108/8/10.1063/1.3499286
http://aip.metastore.ingenta.com/content/aip/journal/jap/108/8/10.1063/1.3499286

Figures

Image of FIG. 1.
FIG. 1.

and characteristics of a virgin FOLED sample with the PEDOT:PSS anode (DMSO 5 wt %).

Image of FIG. 2.
FIG. 2.

(a) , (b) , and (c) characteristics of the E-annealed FOLED using the PEDOT:PSS anode (DMSO 5 wt %).

Image of FIG. 3.
FIG. 3.

Current flows (black solid curve) (a) and emitted EL intensity (blue solid curve) (b) characteristics of the FOLED having the PEDOT:PSS anode (DMSO 7.5 wt %) during the E-annealing process for various treatment voltages. The red dotted curves show the voltage profiles applied to the device for the E-annealing treatments ( : magnitude of treatment voltage pulses and : duration).

Image of FIG. 4.
FIG. 4.

Relative characteristics of the E-annealed FOLEDs using the PEDOT:PSS anodes (DMSO 7.5 wt %) for various annealing conditions: (a) for , (b) for , and (c) for .

Image of FIG. 5.
FIG. 5.

(a) and (b) characteristics of the E-annealed ( for ) FOLEDs using the PEDOT:PSS anodes (DMSO 7.5 and 10.0 wt %).

Image of FIG. 6.
FIG. 6.

Photographs of the operating virgin (left) and E-annealed (right, for ) FOLEDs with the PEDOT:PSS anodes (DMSO 7.5 wt %) under an applied bias of 12 V. The active area of the FOLED is .

Tables

Generic image for table
Table I.

EL characteristics of the E-annealed FOLEDs with the PEDOT:PSS anodes ( for ). : turn-on voltage, : maximum luminance, : maximum power efficiency, and : maximum current efficiency.

Loading

Article metrics loading...

/content/aip/journal/jap/108/8/10.1063/1.3499286
2010-10-25
2014-04-16
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Electrical annealing for flexible organic light-emitting diodes having poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) anodes
http://aip.metastore.ingenta.com/content/aip/journal/jap/108/8/10.1063/1.3499286
10.1063/1.3499286
SEARCH_EXPAND_ITEM