Orientation density along the α and γ fibers averaged over three layers (S = 0, 0.5, 0.75) in the warm rolled Fe–6.5wt.%Si thin sheets.
Shear strain distribution through sheet thickness at different rolling temperatures, calculated by the finite element method.
Constant ϕ2 = 0° and 45° sections of the ODFs of recrystallized Fe–6.5wt.%Si thin sheets rolled at (a) 473 K, (b) 573 K, and (c) 673 K (intensity levels: 1, 2, 3…), and (d) magnetic induction after annealing at 1173 K for 10 min.
(Color online) Orientation image maps with deviation angle of 15° and constant ϕ2 sections of ODFs from EBSD data in 63% recrystallized (a) and just completely recrystallized (b) Fe-6.5wt.%Si thin sheets warm rolled at 473 K.
The (a) average grain size and (b) fraction of different textures within various grain size ranges in just completely recrystallized Fe–6.5wt.%Si thin sheets warm rolled at 473 K.