Effects of Ni addition on the magnetostriction and microstructures of Fe70−xPd30Nix high-temperature ferromagnetic shape memory alloys
Rent:
Rent this article for
USD
10.1063/1.3669915
/content/aip/journal/jap/111/7/10.1063/1.3669915
http://aip.metastore.ingenta.com/content/aip/journal/jap/111/7/10.1063/1.3669915
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

(Color online) The linear saturation magnetostriction λs (×10−6) vs magnetic field (H) λsH curves measured at room temperature of the as-received Fe70−xPd30Nix (x = 2, 4, 6, and 8 at. % Ni) alloys.

Image of FIG. 2.
FIG. 2.

(Color online) The linear magnetostriction (×10−6) at RT (300 K) in parallel (λ) and normal (λ) applied field (H (kOe)) to sample’s longitude of the Fe70−xPd30Nix (x = 2, 4, 6, and 8 at. % Ni) alloys strain-forged to a ∼38% reduction in thickness and then solution-treated (ST) and recrystallization-annealed at 1100 °C for 8 h.

Image of FIG. 3.
FIG. 3.

(Color online) The linear magnetostriction (×10−6) at RT (300 K) in parallel (λ) and normal (λ) applied field (H (kOe)) to sample’s longitude of the Fe70−xPd30Nix (x = 2, 4, 6, and 8 at. % Ni) alloys strain-forged to a ∼38% reduction in thickness and solution-treated (ST) and recrystallization-annealed at 1100 °C for 8 h, quenched in ice brine, and then aged at 500 °C for 100 h.

Image of FIG. 4.
FIG. 4.

X-ray diffraction (XRD) patterns: (a) Fe68Pd30Ni2 (2 at. % Ni), (b) Fe66Pd30Ni4, (c) Fe64Pd30Ni6, and (d) Fe62Pd30Ni8 alloys strain-forged to a ∼38% reduction in thickness, solution-treated (ST) at 1100 °C for 8 h, quenched in ice brine, and aged at 500 °C for 100 h (41.14° denotes diffraction angle 2θ = 41.14°).

Image of FIG. 5.
FIG. 5.

(a)-(d). SEM images of the Fe70−xPd30Nix (x = 2, 4, 6, and 8 at. % Ni) alloys strain-forged to a ∼38% reduction in thickness through solution-treated (ST) and annealed recrystallization at 1100 °C for 8 h, then aged at 500 °C for 100 h.

Loading

Article metrics loading...

/content/aip/journal/jap/111/7/10.1063/1.3669915
2012-02-03
2014-04-18
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Effects of Ni addition on the magnetostriction and microstructures of Fe70−xPd30Nix high-temperature ferromagnetic shape memory alloys
http://aip.metastore.ingenta.com/content/aip/journal/jap/111/7/10.1063/1.3669915
10.1063/1.3669915
SEARCH_EXPAND_ITEM