Effect of pressure loading rate on the crystallographic texture of NdFeB nanocrystalline magnets
Rent:
Rent this article for
USD
10.1063/1.3675173
/content/aip/journal/jap/111/7/10.1063/1.3675173
http://aip.metastore.ingenta.com/content/aip/journal/jap/111/7/10.1063/1.3675173
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

(Color online) (a) XRD patterns, and (b) demagnetization curves measured along c-axis of the deformed bulks at different temperatures. The pressure loading rate is fixed at 150 MPa/min with the maximum applied pressure 1.5 GPa. The XRD pattern and demagnetization curve of isotropic raw MQU-F ribbons are also included. The inset of Fig. 1(b) gives the demagnetization curves measured along and perpendicular to pressure loading direction of the 650 °C deformed magnets.

Image of FIG. 2.
FIG. 2.

(Color online) (a) XRD patterns, and (b) demagnetization curves measured along c-axis of the magnets deformed at 650 °C by different pressure loading rate. The maximum applied pressure is fixed at 1.5 GPa.

Image of FIG. 3.
FIG. 3.

(Color online) Dependence of (BH)max on pressure loading rate of the magnets deformed at 650 °C.

Image of FIG. 4.
FIG. 4.

(Color online) TEM images of the magnets (a) before deformation, and deformed at 650 °C by pressure loading rate of (b) 300 MPa/min, and (c) 50 MPa/min. The thin layers in bright contrast along grain boundaries in (a) are Nd-rich phase.

Loading

Article metrics loading...

/content/aip/journal/jap/111/7/10.1063/1.3675173
2012-02-21
2014-04-19
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Effect of pressure loading rate on the crystallographic texture of NdFeB nanocrystalline magnets
http://aip.metastore.ingenta.com/content/aip/journal/jap/111/7/10.1063/1.3675173
10.1063/1.3675173
SEARCH_EXPAND_ITEM