Room temperature low field magnetoresistance in Sr2FeMoO6/Zn x Fe1− x Fe2O4 composites
Rent:
Rent this article for
USD
10.1063/1.4817024
/content/aip/journal/jap/114/5/10.1063/1.4817024
http://aip.metastore.ingenta.com/content/aip/journal/jap/114/5/10.1063/1.4817024
View: Figures

Figures

Image of FIG. 1.
FIG. 1.

X-ray diffraction pattern of pristine SFMO and SFMO/ZFO composite. Inset of Fig. 1 clearly shows the presence of ZFO peaks.

Image of FIG. 2.
FIG. 2.

(a) High resolution FESEM micrographs of pristine SFMO. (b) EDS pattern of pristine sample. (c) FESEM micrograph of SFMO/ZFO (x = 0.3) composite sample.

Image of FIG. 3.
FIG. 3.

Resistivity versus temperature plots of pristine SFMO and SFMO/ZFO (x = 0.3) composite.

Image of FIG. 4.
FIG. 4.

(a,b). Magnetization versus applied magnetic field plots of pristine SFMO and SFMO/ZFO ( = 0.1, 0.3, 0.5, and 0.7) composites at 300 K and 80 K, respectively.

Image of FIG. 5.
FIG. 5.

Magnetization versus temperature plots of pristine SFMO and SFMO/ZFO ( = 0.1, 0.3, 0.5, and 0.7) of 2 wt. % composites. Inset shows the magnetization versus temperature plots of high content added SFMO: ZFO (5, 10, and 5 wt. %) composites.

Image of FIG. 6.
FIG. 6.

Magnetoresistance versus applied magnetic field plots of pristine SFMO and SFMO/ZFO ( = 0.1, 0.3, 0.5, and 0.7) of 2 wt. % composites at 300 K. Inset shows the MR plots of high content added SFMO: ZFO (5, 10, and 5 wt. %) composites.

Loading

Article metrics loading...

/content/aip/journal/jap/114/5/10.1063/1.4817024
2013-08-02
2014-04-18
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Room temperature low field magnetoresistance in Sr2FeMoO6/ZnxFe1−xFe2O4 composites
http://aip.metastore.ingenta.com/content/aip/journal/jap/114/5/10.1063/1.4817024
10.1063/1.4817024
SEARCH_EXPAND_ITEM