Nonlinear optical properties of Bi2O3-GeO2 glass at 800 and 532 nm
Rent:
Rent this article for
USD
10.1063/1.4818502
/content/aip/journal/jap/114/7/10.1063/1.4818502
http://aip.metastore.ingenta.com/content/aip/journal/jap/114/7/10.1063/1.4818502

Figures

Image of FIG. 1.
FIG. 1.

Absorbance spectra. Samples' thicknesses: 2.1 mm (sample A); 2.0 mm (sample B).

Image of FIG. 2.
FIG. 2.

Kerr gate signals for the two samples studied. The inset shows the Kerr signal for a cell with liquid CS, our reference standard.

Image of FIG. 3.
FIG. 3.

Transmitted intensity as a function of the incident laser intensity. Excitation at 532 nm with laser pulses of 80 ps (a) and 250 ns bursts of 80 ps pulses (b). The solid lines represent fits of Eq. (4) to the experimental points.

Tables

Generic image for table
Table I.

Compositions and samples' parameters: is the samples' length, is the linear index of refraction, and is the linear absorption coefficient.

Generic image for table
Table II.

Nonlinear parameters of the samples: | | is the modulus of the nonlinear refractive index, is the two-photon absorption coefficient, and is the free-carriers absorption cross-section.

Loading

Article metrics loading...

/content/aip/journal/jap/114/7/10.1063/1.4818502
2013-08-16
2014-04-21
Loading

Full text loading...

This is a required field
Please enter a valid email address
752b84549af89a08dbdd7fdb8b9568b5 journal.articlezxybnytfddd
Scitation: Nonlinear optical properties of Bi2O3-GeO2 glass at 800 and 532 nm
http://aip.metastore.ingenta.com/content/aip/journal/jap/114/7/10.1063/1.4818502
10.1063/1.4818502
SEARCH_EXPAND_ITEM