Mutual orientation of the and coordinate systems for the fcc structure of cobalt.
Computed lattice parameters for the elastically deformed fcc film of cobalt in a multilayer structure (111): 1—lattice parameter in the sample plane , 2—perpendicular to the sample plane .
Magnetization of the sample versus the external field oriented in the film plane, : 1—measurement result; 2— for cobalt after subtracting the diamagnetic contribution, approximated by the solid line 3. Inset: curve 2 shown on an enlarged scale.
Computed and experimental values of the effective magnetic anisotropy versus the thickness of the copper interlayers (curve 1 and 2, respectively). The up- and downward pointing arrows indicate the position of the maxima and minima of the resistivity of the corresponding superlattices (111) in the saturation state in the field as a function of .13 The values and were used to calculate .
Computed values of the magnetoelastic anisotropy constants for a series of samples