Chemically mediated diffusion of d-metals and B through Si and agglomeration at Si-on-Mo interfaces
Chemical diffusion and interlayer formation in thin layers and at interfaces is of increasing influence in nanoscopic devices, such as nanoelectronics and reflective multilayer optics. Chemical diffus...
Next Article
Morphology alterations during postsynthesis oxidation of Zn nanowires
Zinc metal nanowires have been oxidized at temperatures of 200–500 °C in ambient air in order to obtain ZnO nanowires. X-ray diffraction investigations reveal a complete transformation from ...

Thermal probing of energy dissipation in current-carrying carbon nanotubes

J. Appl. Phys. 105, 104306 (2009); doi:10.1063/1.3126708

Published 20 May 2009

You are not logged in to this journal. Log in

Li Shi,1 Jianhua Zhou,1 Philip Kim,2 Adrian Bachtold,3 Arun Majumdar,4 and Paul L. McEuen5
1Department of Mechanical Engineering and Center for Nano and Molecular Science and Technology, The University of Texas at Austin, Austin, Texas 78712, USA
2Department of Physics, Columbia University, New York, New York 10027, USA
3Centre d'Investigacions en Nanociencia i Nanotecnologia (Consejo Superior de Investigaciones Científicas–Institut Català de Nanotecnologia), Campus de la Universitat Autònoma de Barcelona (UAB), E-08193 Bellaterra, Spain
4Department of Mechanical Engineering, University of California, Berkeley, California 94720, USA and Materials Science Division, Lawrence Berkeley National Laboratory, Berkeley, California 94720, USA
5Laboratory of Atomic and Solid State Physics, Cornell University, Ithaca, New York 14853 USA
The temperature distributions in current-carrying carbon nanotubes have been measured with a scanning thermal microscope. The obtained temperature profiles reveal diffusive and dissipative electron transport in multiwalled nanotubes and in single-walled nanotubes when the voltage bias was higher than the 0.1–0.2 eV optical phonon energy. Over 90% of the Joule heat in a multiwalled nanotube was found to be conducted along the nanotube to the two metal contacts. In comparison, about 80% of the Joule heat was transferred directly across the nanotube-substrate interface for single-walled nanotubes. The average temperature rise in the nanotubes is determined to be in the range of 5–42 K per microwatt Joule heat dissipation in the nanotubes. ©2009 American Institute of Physics
History: Received 10 December 2008; accepted 3 April 2009; published 20 May 2009
Permalink: http://link.aip.org/link/?JAPIAU/105/104306/1
BUY THIS ARTICLE   (US$24)
Download HTML Download Sectioned HTML Download PDF (373 kB) View Cart

KEYWORDS and PACS

Keywords
PACS
  • 66.70.Lm
    Nonelectronic thermal conduction and heat-pulse propagation in other solids
  • 65.80.+n
    Thermal properties of small particles, nanocrystals, nanotubes
  • YEAR: 2009

RELATED DATABASES


To view database links for this article,
you need to log in.
To view database links for this article,
you need to log in.

PUBLICATION DATA

ISSN:
0021-8979 (print)   1089-7550 (online)
Publisher:
AIP is a member of CrossRef AIP

REFERENCES (41)
View in Separate Window/Tab
For access to fully linked references, you need to log in. For access to fully linked references, you need to Log in.
  1. S. J. Tans, M. H. Devoret, R. J. A. Groeneveld, and C. Dekker, Nature (London) 394, 761 (1998).
  2. M. Bockrath, D. H. Cobden, P. L. McEuen, N. G. Chopra, A. Zettl, A. Thess, and R. E. Smalley, Science 275, 1922 (1997).
  3. A. Javey, J. Guo, Q. Wang, M. Lundstrom, and H. J. Dai, Nature (London) 424, 654 (2003).
  4. J. Y. Park, S. Rosenblatt, Y. Yaish, V. Sazonova, H. Ustunel, S. Braig, T. A. Arias, P. W. Brouwer, and P. L. McEuen, Nano Lett. 4, 517 (2004).
  5. T. Ando, T. Nakanishi, and R. Saito, J. Phys. Soc. Jpn. 67, 2857 (1998).
  6. T. Ando and T. Nakanishi, J. Phys. Soc. Jpn. 67, 1704 (1998).
  7. P. L. McEuen, M. Bockrath, D. H. Cobden, Y. G. Yoon, and S. G. Louie, Phys. Rev. Lett. 83, 5098 (1999).
  8. B. Gao, Y. F. Chen, M. S. Fuhrer, D. C. Glattli, and A. Bachtold, Phys. Rev. Lett. 95, 196802 (2005).
  9. M. S. Purewal, B. H. Hong, A. Ravi, B. Chandra, J. Hone, and P. Kim, Phys. Rev. Lett. 98, 186808 (2007).
  10. P. G. Collins, M. Hersam, M. Arnold, R. Martel, and P. Avouris, Phys. Rev. Lett. 86, 3128 (2001).
  11. Z. Yao, C. L. Kane, and C. Dekker, Phys. Rev. Lett. 84, 2941 (2000).
  12. P. C. Collins, M. S. Arnold, and P. Avouris, Science 292, 706 (2001).
  13. E. Pop, D. Mann, J. Cao, Q. Wang, K. Goodson, and H. J. Dai, Phys. Rev. Lett. 95, 155505 (2005).
  14. P. Sundqvist, F. J. Garcia-Vidal, F. Flores, M. Moreno-Moreno, C. Gomez-Navarro, J. S. Bunch, and J. Gomez-Herrero, Nano Lett. 7, 2568 (2007).
  15. M. Lazzeri and F. Mauri, Phys. Rev. B 73, 165419 (2006).
  16. L. E. F. Foa Torres and S. Roche, Phys. Rev. Lett. 97, 076804 (2006).
  17. E. Pop, D. Mann, Q. Wang, K. Goodson, and H. J. Dai, Nano Lett. 6, 96 (2006).
  18. T. Y. Choi, D. Poulikakos, J. Tharian, and U. Sennhauser, Nano Lett. 6, 1589 (2006).
  19. Z. L. Wang, D. W. Tang, X. B. Li, X. H. Zheng, W. G. Zhang, L. X. Zheng, Y. T. T. Zhu, A. Z. Jin, H. F. Yang, and C. Z. Gu, Appl. Phys. Lett. 91, 123119 (2007).
  20. A. W. Bushmaker, V. V. Deshpande, M. W. Bockrath, and S. B. Cronin, Nano Lett. 7, 3618 (2007).
  21. G. E. Begtrup, K. G. Ray, B. M. Kessler, T. D. Yuzvinsky, H. Garcia, and A. Zettl, Phys. Rev. Lett. 99, 155901 (2007).
  22. L. Shi, O. Kwon, A. C. Miner, and A. Majumdar, J. Microelectromech. Syst. 10, 370 (2001).
  23. L. Shi, S. Plyasunov, A. Bachtold, P. L. McEuen, and A. Majumdar, Appl. Phys. Lett. 77, 4295 (2000).
  24. L. Shi and A. Majumdar, ASME Trans. J. Heat Transfer 124, 329 (2002).
  25. A. Majumdar, Annu. Rev. Mater. Sci. 29, 505 (1999).
  26. L. Shi, Ph.D. thesis, University of California, Berkeley, 2001.
  27. P. Kim, L. Shi, A. Majumdar, and P. L. McEuen, Physica B 323, 67 (2002).
  28. B. Bourlon, C. Miko, L. Forro, D. C. Glattli, and A. Bachtold, Semicond. Sci. Technol. 21, S33 (2006).
  29. F. P. Incropera, D. P. Dewitt, T. L. Bergman, and A. S. Lavine, Fundamentals of Heat and Mass Transfer, 6th ed. (Wiley, Hoboken, NJ, 2007).
  30. For the ac electrical heating case, Eq. (1) can be solved using the impulse theorem (Refs. 19,40) The obtained solution reveals that the characteristic frequency corresponding to the thermal time constant (tauNT) of the SWNT is fNT=1/2pitauNT=(pik/L2+g/piA)/4rhoC. fNT is estimated to be of the order of 1010  Hz using k[approximate]3000  W/m K (Refs. 17,31,32) g[approximate]0.2  W/m K (Refs. 37,38), and rho and C of graphite (Ref. 29). During electrical heating of the SWNT, appreciable temperature rise is expected to occur in the supporting substrate only within a distance of about 5L from the SWNT. The thermal time constant of the substrate volume with appreciable temperature rise is tausub=(5L)2/4alpha. The upper limit of tausub is about 70  µs based on the smaller thermal diffusivity (alpha) value of the silicon oxide film and the silicon substrate. This upper limit corresponds to the lower limit of the substrate characteristic frequency of fsub[approximate]2000  Hz.
  31. C. H. Yu, L. Shi, Z. Yao, D. Y. Li, and A. Majumdar, Nano Lett. 5, 1842 (2005).
  32. P. Kim, L. Shi, A. Majumdar, and P. L. McEuen, Phys. Rev. Lett. 87, 215502 (2001).
  33. C. W. Chang, A. M. Fennimore, A. Afanasiev, D. Okawa, T. Ikuno, H. Garcia, D. Y. Li, A. Majumdar, and A. Zettl, Phys. Rev. Lett. 97, 085901 (2006).
  34. M. Fujii, X. Zhang, H. Q. Xie, H. Ago, K. Takahashi, T. Ikuta, H. Abe, and T. Shimizu, Phys. Rev. Lett. 95, 065502 (2005).
  35. H. Y. Chiu, V. V. Deshpande, H. W. C. Postma, C. N. Lau, C. Miko, L. Forro, and M. Bockrath, Phys. Rev. Lett. 95, 226101 (2005).
  36. For the case that the NT length (L) is much longer than the 1  µm thickness (d) of the SiO2 film, RS approaches the following solution that ignores temperature variation along the NT axis, RS,2D=(1/b)[integral]<sub>0</sub><sup>b</sup>[integral]<sub>0</sub><sup>b</sup>[sin(sb)/pibkfs2][tanh(sd)+(kf/ks)tanh(sds)/1+(kf/ks)tanh(sd)tanh(sds)]cos(xs)dsdx (Ref. 41), where b is the half width of the contact line between the NT and the SiO2 film, kf and ks are the thermal conductivity of the SiO2 film and Si substrate, respectively, and ds=500  µm is the thickness of the Si substrate. For b=0.1–10  nm, RS,2D is in the range of 1.4–1.375  K m/W. Because of the ~100 times higher ks than kf, RS,2D decreases for only about 1% when ds is reduced from 500 to 0  µm, suggesting that RS,2D is dominated by the spreading resistance in the SiO2 film. When L is only about three times longer than d in our measurements, RS is expected to be slightly smaller than RS,2D because of additional heat spreading to the substrate in the direction along the NT axis.
  37. H. Maune, H. Y. Chiu, and M. Bockrath, Appl. Phys. Lett. 89, 013109 (2006).
  38. E. Pop, D. A. Mann, K. E. Goodson, and H. J. Dai, J. Appl. Phys. 101, 093710 (2007).
  39. R. Prasher, Nano Lett. 5, 2155 (2005).
  40. L. Lu, W. Yi, and D. L. Zhang, Rev. Sci. Instrum. 72, 2996 (2001).
  41. G. Chen, Nanoscale Energy Transport and Conversion: A Parallel Treatment of Electrons, Molecules, Phonons, and Photons (Oxford University Press, New York, 2005).

CITING ARTICLES
For access to citing articles, you need to log in.
For access to citing articles, you need to Log in.


Copyright © American Institute of Physics